Other name: Non-asbestos composite Gasket Sheet, Non-asbestos composite sheet, Reinforced non-asbestos sheet, Non-asbestos composite beater sheet, Non-asbestos beater sheet, non-asbestos Reinforced sheet

Manufactured from non-asbestos beater sheet(100% not contain asbestos)with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.

This series include:

1) Reinforced non-asbestos Composite Sheet
2) Reinforced non-asbestos Composite Sheet with Both Size Coating Graphite
3) Two or more Layers Steel Inserted Reinforced Non-Asbestos Sheet
4) Reinforced Non-Asbestos Sheet With Both Size Coating Silicon Resin (anti stick)

Available Size: Thickness:1.0mm ~ 3.0mm
400mm x 1000mm ,500mm x 1000mm ,500mm x 1200mm ,500mm x 1500mm
510mm x 1016mm ,510mm x 1530mm ,1000mm x 1000mm ,1000mm x 1500mm
Color: Gray, Black
The other size is optional or according to the requirements of customers.
Product Date Sheet

Item		Standard data
Density g/cm³		1.3～1.5
working temperature ℃		150～300
Compressibility %		10±5
Recovery ≥ %		40
Sealing performance		<0.5cm3/min
causticity		Cusp no rusty
Tensile strength MPa ≥		12.7
Compressive Strength MPa ≥		80.0
Carbon content ≥ %		98
Ash content ＜%		1
With the temperature of 150±2℃,Soaking 20# fluid oil for 5 hours, MPa≥	oil absorption %≤	25
	Thickness-increasing %≤	0～10
	Stripping performance	No stripe
With the temperature of 15 to 30℃,Soaking 75# kerosene for 5 hours, MPa≥	oil absorption %≤	15
	Thickness-increasing %≤	0～15
	Stripping performance	No stripe
With the temperature of 100℃,Soaking distilled water for 5 hours, MPa≥	water absorption %≤	15
	Thickness-increasing %≤	0～15
	Stripping performance	No strip